PE Heat Shrink Cable End Caps for Cable Caps

• Customization: Available
• Application: Insulators, Electrical Winding Insulation, Winding Wire Coating Insulation, Electrical Base, Shell, Motor, Insulating Varnish, Switch Baseplate, Cables etc
• Color: All Colors
• Model NO.: SB-WRSFM
• Material: Polyolefin
• Maximum Voltage: <10KV
• Thermal Rating: A 105
• Working Temp: -45~+105 C
• Shrink Temp: 110~130c
• Shrink Ratio: 2:1
• Standard Color: Black
• Cable Size: 6~240mm
• Length: 22~270mm
• Type: Insulation Sleeve & Tube
• Chemistry: Organic Insulation
• Classification: Organic Insulating Material
• Certification: ISO9001, IATF 16949
• Brand: Sunbow
• Transport Package: Carton Package or Pallet Package
• Specification: ID11~250MM
• Trademark: SUNBOW
• Origin: Shenzhen, China
• HS Code: 3917310000
• Production Capacity: 500000pieces/Month

Product Description

PE Heat Shrink Cable End Caps for Cable Caps

Model Number: SB-WRSFM
Heat shrink end caps are a simple yet effective method for sealing cable ends, pipe, conduit or other similar objects.

Features
2:1 shrink ratio   
Superior resistance to weathering
Resistant to common fluids
Standard adhesive liner provides coated hot melt adhesive resists continuous operating temperature
Shrink temperature: start at 110ºC, and fully recovered at 130ºC

 Dimension

Size	Size after recovery(mm)		Size as supplied (mm)			Cable sizes(mm)
	Inner Diameter	Wall thickness	Inner Diameter	Wall thickness	length	Outer Diameter
Φ 11	≤6.5	1.1±0.1	≥11	0.7±0.2	≥22	Φ6-9
Φ 16	≤8.0	2.5±0.1	≥16	1.2±0.2	≥70	Φ9-14
Φ 20	≤8.0	2.5±0.1	≥20	1.2±0.2	≥70	Φ9-17
Φ 25	≤11	2.5±0.1	≥25	1.2±0.2	≥80	Φ12-22
Φ 32	≤17	2.6±0.1	≥32	1.5±0.2	≥90	Φ17-27
Φ 40	≤15	2.8±0.1	≥40	1.5±0.2	≥90	Φ20-35
Φ 55	≤25	2.8±0.1	≥55	1.5±0.2	≥125	Φ28-45
Φ 75	≤30	3.2±0.1	≥75	1.8±0.2	≥145	Φ40-65
Φ 100	≤42	3.5±0.1	≥100	1.8±0.2	≥140	Φ50-90
Φ 120	≤59	3.5±0.1	≥120	1.8±0.2	≥155	Φ70-110
Φ 140	≤63	4.0±0.1	≥140	2.0±0.2	≥180	Φ90-130
Φ 250	≤94	4.0±0.1	≥250	2.0±0.2	≥270	Φ120-240

Technical Data

Property	Test Method	Standard Value
Operating temperature	IEC 216	-45ºC to+105ºC
Tensile strength	ASTM-D 2671	≥13MPa
Elongation at break	ASTM-D 2671	≥300%
Tensile strength after aging	ASTM-D-2671/120ºC,168hrs	≥10MPa
Elongation at break after aging	ASTM-D-2671/120ºC,168hrs	≥240%
Dielectric strength	IEC 243	≥15kV/mm
Volume resistance	ASTM-D-2303	≥1×1013Ohm.cm
Dielectric constant	IEC 250	3.0
Radial shrinkage	-	≥50%
Eccentricity	ASTM-D-2671	≤35%
Low Temperature Flexibility	ASTM-D-2671	-40ºC, 4hrs, no cracking
Minimum shrink temperature	-	90ºC
Minimum fully recovered temperature	-	130ºC