Heat Shrink End Cap with Adhesive Black shrinkable caps for Cable Termination Protection
Model Number: SB-WRSFM
Heat shrink end caps are a simple yet effective method for sealing cable ends, pipe, conduit or other similar objects.
Features
2:1 shrink ratio
Superior resistance to weathering
Resistant to common fluids
Standard adhesive liner provides coated hot melt adhesive resists continuous operating temperature
Shrink temperature: start at 110ºC, and fully recovered at 130ºC
Dimension
Size |
Size after recovery(mm) |
Size as supplied (mm) |
Cable sizes(mm) |
|||
Inner Diameter |
Wall thickness |
Inner Diameter |
Wall thickness |
length |
Outer Diameter |
|
Φ 11 |
≤6.5 |
1.1±0.1 |
≥11 |
0.7±0.2 |
≥22 |
Φ6-9 |
Φ 16 |
≤8.0 |
2.5±0.1 |
≥16 |
1.2±0.2 |
≥70 |
Φ9-14 |
Φ 20 |
≤8.0 |
2.5±0.1 |
≥20 |
1.2±0.2 |
≥70 |
Φ9-17 |
Φ 25 |
≤11 |
2.5±0.1 |
≥25 |
1.2±0.2 |
≥80 |
Φ12-22 |
Φ 32 |
≤17 |
2.6±0.1 |
≥32 |
1.5±0.2 |
≥90 |
Φ17-27 |
Φ 40 |
≤15 |
2.8±0.1 |
≥40 |
1.5±0.2 |
≥90 |
Φ20-35 |
Φ 55 |
≤25 |
2.8±0.1 |
≥55 |
1.5±0.2 |
≥125 |
Φ28-45 |
Φ 75 |
≤30 |
3.2±0.1 |
≥75 |
1.8±0.2 |
≥145 |
Φ40-65 |
Φ 100 |
≤42 |
3.5±0.1 |
≥100 |
1.8±0.2 |
≥140 |
Φ50-90 |
Φ 120 |
≤59 |
3.5±0.1 |
≥120 |
1.8±0.2 |
≥155 |
Φ70-110 |
Φ 140 |
≤63 |
4.0±0.1 |
≥140 |
2.0±0.2 |
≥180 |
Φ90-130 |
Φ 250 |
≤94 |
4.0±0.1 |
≥250 |
2.0±0.2 |
≥270 |
Φ120-240 |
Heat Shrink End Cap with Adhesive Black shrinkable caps for Cable Termination Protection
Technical Data
Property |
Test Method |
Standard Value |
Operating temperature |
IEC 216 |
-45ºC to+105ºC |
Tensile strength |
ASTM-D 2671 |
≥13MPa |
Elongation at break |
ASTM-D 2671 |
≥300% |
Tensile strength after aging |
ASTM-D-2671/120ºC,168hrs |
≥10MPa |
Elongation at break after aging |
ASTM-D-2671/120ºC,168hrs |
≥240% |
Dielectric strength |
IEC 243 |
≥15kV/mm |
Volume resistance |
ASTM-D-2303 |
≥1×1013.cm |
Dielectric constant |
IEC 250 |
3.0 |
Radial shrinkage |
- |
≥50% |
Eccentricity |
ASTM-D-2671 |
≤35% |
Low Temperature Flexibility |
ASTM-D-2671 |
-40ºC, 4hrs, no cracking |
Minimum shrink temperature |
- |
90ºC |
Minimum fully recovered temperature |
- |
130ºC |